Permabond TA 4610
Permabond® TA4246 is a structural two-component acrylate adhesive that cures quickly at room temperature and is resistant to high temperatures.
documents
HS code:
3506.9190000
Description
PERMABOND® TA4610 is a two-component, reinforced acrylic adhesive with a 1:1 mix ratio. It is specifically designed for bonding low surface energy plastics such as polypropylene and polyethylene—no primer or surface preparation is required. This adhesive can also be used on a variety of other materials such as metals or composites and is ideal for a wide range of surfaces.
Suitable substrates
It bonds a wide range of materials:
- Plastics with low surface energy (polyolefins) in particular, e.g., polypropylene (PP), polyethylene (PE)
- metals
- composite materials
- Different surfaces
Advantages of Permabond® TA4610
- Rapid curing at room temperature
- No primer required
- High impact resistance
- Good resistance to chemicals
- Excellent water resistance (sticks underwater)
Note on surface pretreatment
For almost all materials, cleaning the surface is sufficient (except for aluminum, for example, which must first be roughened). If there are still traces of release agent on polyolefin plastics, these can be cleaned with Cleaner A before bonding and then dried.
product specifications
| product information | |
|---|---|
| container | 50 ml or 400 ml |
| manufacturer | Permabond Engineering Adhesives Ltd |
| mixing ratio | 1:1 |
| country of origin | Italy |
| Processing time (pot life) at 25°C | 5-8 minutes |
| Storage temperature (°C) | 2-7 |
| Operating temperature (°C) | -55 to 100 |
| Shear strength ISO ISO4587 in N/mm² | |
|---|---|
| polypropylene | 5-8 N/mm² |
| polyethylene | 3-6 N/mm² |
| aluminum | 3-6 N/mm² |
| PTFE | 1.5 N/mm² |
| ABS | >4 N/mm² |
| polycarbonate | >5 N/mm² |
| polyvinyl chloride | >5 N/mm² |
| EPDM | 3-5 N/mm² |
| PA6 | 3-5 N/mm² |
| Physical properties A | |
|---|---|
| Chemical group (A) | methacrylate |
| Color (A) | Grayish white |
| Viscosity (A) | 200,000–500,000 |
| Specific gravity (A) | 1.0 |
| UFI Part A | 7030-N0MT-F00Q-TWK6 |
| Physical properties B | |
|---|---|
| Chemical group (B) | methacrylate |
| Color (B) | Colorless |
| Viscosity (B) | 20,000-30,000 |
| Specific gravity (B) | 1.0 |
| UFI Part B | S330-50A6-S007-G858 |
| Properties of the bond | |
|---|---|
| Maximum gap filling capacity up to | 1.0 mm |
| Handling strength at 23°C | 40-50 minutes |
| Functional strength | 6-8 hours |
| Final strength at 23°C | 36-48 hours |