Merbenit SK212
Merbenit SK212 - A flexible adhesive with high initial tack and high strength.
Merbenit SK212 - Windshield adhesive with high initial adhesion (FMVSS 212).
Elastic adhesive with high initial tack and high strength. Specifically designed for windshield replacement and general bonding of glass in cabins and vehicles, certified to FMVSS 212, easy to apply.
- Very high initial adhesion, adjustable
- Without the addition of solvents, isocyanates, silicones,
- phthalates
- Excellent sealing properties
- Very broad range of adhesion
Merbenit SK212 - Windshield adhesive with high initial adhesion (FMVSS 212)
Elastic adhesive with high initial tack and high strength. Specifically designed for windshield replacement and general bonding of glass in cabins and vehicles, certified to FMVSS 212, easy to apply.
product benefits
- Very high initial adhesion, adjustable
- Without the addition of solvents, isocyanates, silicones,
- phthalates
- Excellent sealing properties
- Very broad range of adhesion
- Low odor
- Paint-compatible
- For powder coating and thermal painting, up to +200°C for short periods
- consistent
- Non-corrosive to surfaces
- Shock- and vibration-resistant (shock-absorbing)
- High electrical resistance, suitable for car bodies made of
- Aluminum, vehicles equipped with GPS or
- Driver assistance systems
Examples of use
Bonding of windows in automotive, railcar, and cabin construction. Bonding applications that cannot be supported and require rapid further processing. Flexible, immediately load-bearing bonds in the fields of metalworking, equipment and machinery manufacturing, plastics, ventilation, and air conditioning technology, as well as automotive, railcar, vehicle, and container construction.
Adhesion spectrum
Low-odor, compatible with paint systems; resistant to powder and thermal coating at temperatures up to +200°C for short periods; non-corrosive on surfaces; impact- and vibration-resistant (shock-absorbing) High electrical resistance, suitable for aluminum car bodies, vehicles equipped with GPS or driver assistance systems Technical Data Chemical Basis Silane-modified polymer Curing Mechanism 1K moisture-curing Consistency Stable Processing Time Max. 15 min. Cure depth after 24h approx. 3.5 mm Cure depth after 48h approx. 4.5 mm Shore A hardness, DIN ISO 48-4 approx. 55 Tensile strength DIN 53504 S2* approx. 2.8 N/mm² Modulus at 100% elongation, DIN 53504 S2 * approx. 2.0 N/mm² Elongation at break, DIN 53504 S2 * approx. 225% Tensile shear strength 2.2 N/mm² Density 1.35 ± 0.05 g/cm³ Volume change, DIN EN ISO 10563 ≤ 3% Temperature resistance after curing - 40 °C to + 90 °C Application temperature + 5 °C to + 40 °C Initial adhesion approx. 3700 Pa Volume resistivity p, DIN EN 62631-3-1 10^12 Ω*cm All measurements were performed under standard conditions (23 °C and 50% relative humidity). * The data is based on measurements taken after 3 months. Application examples Bonding of windows in automotive, railcar, and cabin construction. Bonding applications that cannot be supported and require rapid further processing. Flexible, immediately load-bearing bonds in the fields of metal, apparatus, and mechanical engineering; plastics, ventilation, and air conditioning technology; and body, railcar, vehicle, and container construction. Adhesion spectrum: Well-suited materials include metals, powder-coated, painted, galvanized, anodized, chromated, or hot-dip galvanized surfaces, various plastics, ceramics, concrete, plaster, wood, glass, painted surfaces, etc. Due to the wide variety of different plastics and their compositions, as well as materials prone to stress cracking (PC, PMMA), preliminary tests are recommended. Please also refer to the section
Standards & Certifications
- EMICODE EC1Plus
- Euro NCAP frontal impact at 64 km/h
- Eurofins IAC Gold
- FMVSS 212: Acceleration time 60 seconds
product specifications
| Physical properties | |
|---|---|
| density | 1.35 g/cm³ |
| Hardness (Shore A) | approx. 55 |
| Cured layer thickness after 24 hours | approx. 3.5 mm |
| Color | black |
| curing technology | Moisture-curing |
| Chemical group | Silane-modified polymer |
| product information | |
|---|---|
| container | 290 ml cartridge or 600 ml pouch |
| tensile strength | approx. 2.8 N/mm² |
| Temperature range (°C) | -40 °C to +90 °C |
| consistency | Stable |
| Performance at ultimate strength | |
|---|---|
| elongation at break | approx. 225% |
| Uncategorized | |
|---|---|
| processing temperature | +5 °C to +40 °C |
| Stress at 100% elongation | approx. 2.0 N/mm² |
| change in volume | ≤ 3% |
| Number of components | 1K |