Merbenite 2K60
Merbenit 2K60 - Merbenit 2K60 is a permanently elastic two-component adhesive that develops strength very quickly and offers excellent adhesion, particularly on plastics that are difficult to bond.
Merbenit 2K60 - A permanently elastic two-component adhesive with rapid strength development.
Merbenit 2K60 is a permanently elastic two-component adhesive that develops strength very quickly and offers excellent adhesion, particularly on plastics that are difficult to bond.
- Quick setting, fully cured after 30 minutes
- Paint-compatible
- Easy processing
- Corrosion-resistant
- Free of solvents, isocyanates, and silicones
Internal reference:
92-2K60.KT.ML400.GR
Merbenit 2K60 - Permanently elastic two-component adhesive with rapid strength development
Merbenit 2K60 is a permanently elastic two-component adhesive that develops strength very quickly and offers excellent adhesion, particularly on plastics that are difficult to bond.
product benefits
- Quick setting, fully cured after 30 minutes
- Paint-compatible
- Easy processing
- Corrosion-resistant
- Free of solvents, isocyanates, and silicones
- Low odor
- Non-corrosive to surfaces
- Shock- and vibration-resistant (shock-absorbing)
- Very broad range of adhesion
- Excellent sealing properties
Examples of use
Flexible bonding for use in metalworking, equipment and machinery manufacturing, plastics, ventilation and air conditioning technology, as well as automotive, railcar, vehicle, and container construction. Rapid curing allows for quick further processing of the bonded parts. The neutral-curing polymer enables application without thermal or chemical pretreatment of the parts to be joined. Joints that compensate for dimensional tolerances.
Adhesion spectrum
Excellent sealing properties Technical data Chemical composition Silane-modified polymer Curing mechanism 2-component moisture-curing Consistency Paste-like Working time Max. 4 min. Shore A hardness, DIN ISO 7619-1 48 Tensile strength after 1 hour Approx. 1.3 N/mm² Tensile strength, DIN 53504 S2* approx. 3.5 N/mm² Modulus at 100% elongation, DIN 53504 S2 * approx. 2.0 N/mm² Elongation at break, DIN 53504 S2 * approx. 150% Tensile shear strength approx. 3.0 N/mm² Volume change, DIN EN ISO 10563 ≤ 8% Temperature resistance after curing -40 °C to +90 °C Application temperature +5 °C to +40 °C Substrate temperature +5 °C to +40 °C Density, Component A 1.35 ± 0.05 g/cm³ Density, Component B 1.40 ± 0.05 g/cm³ All measurements were performed under standard conditions (23 °C and 50% relative humidity). * The data is based on measurements taken after 3 months. Application Examples Flexible bonding in the fields of metal, apparatus, and mechanical engineering; plastics, ventilation, and air conditioning technology; and bodywork, railcar, vehicle, and container construction. Rapid curing allows for quick further processing of the bonded parts. The neutral-curing polymer enables application without thermal or chemical pretreatment of the joint. Tolerance-compensating bond. Adhesion spectrum: Suitable materials include metals, powder-coated, painted, galvanized, anodized, chromated, or hot-dip galvanized surfaces, various plastics, ceramics, stone, concrete, and wood. Due to the wide variety of different plastics and compositions, as well as materials prone to stress cracking, preliminary tests are recommended.
product specifications
| Physical properties | |
|---|---|
| density | 1.35 / 1.40 g/cm³ |
| Hardness (Shore A) | 48 |
| Color | gray |
| curing technology | Moisture-curing |
| Chemical group | Silane-modified polymer |
| product information | |
|---|---|
| tensile strength | approx. 3.5 N/mm² |
| Temperature range (°C) | -40 °C to +90 °C |
| container | 2 x 200 ml cartridges |
| consistency | Pasty |
| Performance at ultimate strength | |
|---|---|
| elongation at break | approx. 150% |
| Uncategorized | |
|---|---|
| processing temperature | +5 °C to +40 °C |
| Stress at 100% elongation | approx. 2.0 N/mm² |
| change in volume | ≤ 8% |
| Number of components | 2K |