Permabond TA 4522
PERMABOND® TA4522 is a low-odor, 1:1 mix ratio, two-component acrylate adhesive. It is suitable for bonding a wide range of materials, including plastics, fiberglass, ceramics, wood, metal, and other substrates.
documents
Internal reference:
49-4522.KT.G050
HS code:
49-4522.KT.G050
Description
PERMABOND® TA4522 is a low-odor, 1:1 mix ratio, two-component acrylic adhesive. It is suitable for bonding a wide range of materials, including plastics, fiberglass, ceramics, wood, metal, and other substrates. It is convenient to use in an easy-to-dispense cartridge with a mixing nozzle or can be applied bead-to-bead* without a static mixer. The non-aggressive formulation of this product minimizes the likelihood of stress cracking in sensitive plastics.
product specifications
| Physical properties | |
|---|---|
| Color | green |
| product information | |
|---|---|
| manufacturer | Permabond Engineering Adhesives Ltd |
| container | 50 ml |
| mixing ratio | 1:1 |
| country of origin | Italy |
| Operating temperature (°C) | -55 to 130 |
| Additional features | |
|---|---|
| Nozzle life @23°C | 4-7 minutes |
| Mechanical properties | |
|---|---|
| Hardness (Shore D) | 70-75 |
| Shear strength ISO ISO4587 in N/mm² | |
|---|---|
| polyvinyl chloride | 4-5 N/mm² |
| PMMA | 2-3 N/mm² |
| ABS | 2-3 N/mm² |
| aluminum | 14-16 N/mm² |
| curing values | |
|---|---|
| ultimate strength | 24-48 hours |
| Physical properties A | |
|---|---|
| Chemical group (A) | urethane methacrylate |
| Color (A) | White |
| Viscosity (A) | 3000-6000 |
| Specific gravity (A) | 1.1 |
| Physical properties B | |
|---|---|
| Chemical group (B) | urethane methacrylate |
| Color (B) | Green/Blue |
| Viscosity (B) | 3000-6000 |
| Specific gravity (B) | 1.1 |
| Performance at ultimate strength | |
|---|---|
| Shear strength polycarbonate | 4-6 N/mm² |
| steel | 21-23 N/mm² |
| Properties of the bond | |
|---|---|
| Maximum gap filling capacity up to | 0.5 mm |
| Handling strength at 23°C | 10-15 minutes |